1420 High performance structural bonding acrylic adhesive
Two component, blue, rigid, super fast curing methyl acrylic acid adhesive.Suitable for plastic, metal and composite adhesive, high viscosity, high thixotropic, not vertical flow, Mixing ratio 10:1, Operation time 3-4 minutes, time 6-10 minutes;strength:75% . Especially suitable for bonding of composite materials, without surface treatment can reach the highest strength, good toughness, good shock resistance, fatigue resistance. Meet the demand of mass production line.
Typical Applications
Transport vehicles, notebook computer, mobile phone and other products such as structural adhesive bonding electrons.
Bonding material: ABS, glass steel, polyester (DCPD modified) polystyrene, polyethylene ester, PVC, polyurethane, coating
Carbon steel, aluminum and stainless steel recommended HuiTian primer 1020.
| Item |
Unit |
Typical Value |
| Color |
Component A |
|
White |
| Component B |
|
Blue |
| Component of Basic Materials |
|
acrylic acid |
| Density |
Component A |
g/cm3 |
0.96 |
| Component B |
1.13 |
| Viscosity |
Component A |
mPa*s |
160000 |
| Component B |
140000 |
| After Mixed |
|
| Mix Ratio by weight (A:B) |
|
10:1 |
| Handing Curing Time |
Min |
25 |
| Initial Curing Time |
Hour |
0.5 |
| Full Curing Time |
Hour |
24 |
| Tensile Strength |
After Curing |
Mpa |
20 |
| Elongation at break |
% |
|
| Hardness |
Shore A |
|
| Volume Resistivity |
Ω*cm |
|
| Dielectric Strength |
KV/mm |
|
| Flame Retardant Rating |
|
UL94 V-1 |
| Work Temperature |
℃ |
-55~121 |
Medium resistance
Resistance PH 3-10 acid, hydrocarbons, salt solution. Not resistant to polar solvent, acid and alkali.
How to use
Surface treatment: Remove dust, water, oil from surface; maintain the adhesive surface clean, carbon steel, aluminum and stainless steel recommended Huitian primer to reach 1020 best bonding results.