1420 High performance structural bonding acrylic adhesive
Typical Applications
Transport vehicles, notebook computer, mobile phone and other products such as structural adhesive bonding electrons.
Bonding material: ABS, glass steel, polyester (DCPD modified) polystyrene, polyethylene ester, PVC, polyurethane, coating
Carbon steel, aluminum and stainless steel recommended HuiTian primer 1020.
Item | Unit | Typical Value | ||
Color | Component A | White | ||
Component B | Blue | |||
Component of Basic Materials | acrylic acid | |||
Density | Component A | g/cm3 | 0.96 | |
Component B | 1.13 | |||
Viscosity | Component A | mPa*s | 160000 | |
Component B | 140000 | |||
After Mixed | ||||
Mix Ratio by weight (A:B) | 10:1 | |||
Handing Curing Time | Min | 25 | ||
Initial Curing Time | Hour | 0.5 | ||
Full Curing Time | Hour | 24 | ||
Tensile Strength | After Curing | Mpa | 20 | |
Elongation at break | % | |||
Hardness | Shore A | |||
Volume Resistivity | Ω*cm | |||
Dielectric Strength | KV/mm | |||
Flame Retardant Rating | UL94 V-1 | |||
Work Temperature | ℃ | -55~121 |
Surface treatment:
Remove dust, water, oil from surface; maintain the adhesive surface clean, carbon steel, aluminum and stainless steel recommended Huitian primer to reach 1020 best bonding results.
Mixing Adhesive:
Through a fixed mixing ratio of the mixing nozzle mix, with manual, pneumatic or equipment gluing
Gluing:
This product at 18 ℃ -27 ℃ environment construction to achieve the most ideal curing effect, below 18 ℃ curing slower, more than 27 ℃ curing faster. Effects of A and B components of the viscosity is affected by temperature, in order to ensure the measurement / consistent, effect of mixing equipment, the two components in the storage temperature to maintain a constant.
Gluing work must finish in operation time. Operation before the end of time, glue and positioning of the work piece to accurately completed, then keep the work piece in a fixed state until the end to remove positioning time.
Clean:
Before curing is easier to clean, wipe the lotion, overflow adhesive residue available containing citric acid, terpene resin or NMP degreasing agent scrub in order to achieve the best results. If the layer has been cured, carefully will layer off, and wipe the lotion good cleaning effect.
Matters need attention
1.This product is flammable, away from heat and flame, spark store or use.
2.Not including the adhesive materials: PP, PE, POM, PTFE, copper, brass
3.All stainless steel, aluminum, mixing equipment be Teflon or PE material. Filler, pump shall not use copper or copper alloy. The sealing ring must use Teflon, Teflon coated PVC, PE/PP, VITON, NBR, chloroprene rubber or other elastic body shall not be.
4.This product is curing very fast, generates a lot of heat when mass mixing, and may be accompanied by release of gas, steam and other volatiles. Therefore, should be in every time limited quantity in mixed operation time can run out, and the adhesive thickness is controlled within 3.2mm
Package
50ml/ Double tube, 12 double tube /carton.
380ml/ double tube, 12 Double tubes /carton
Storage
1.Store it in dry and shady places at the temperature of 12~24℃ is best
2.A component Ø Storage life: 12 months,,B component 9months
3. Could not frozen storage