● Product Features:
Ø 4010 RTV-2 adhesive sealing silicone is a two-component, semi flowing, black room temperature vulcanized silicone.
Ø Cured adhesive for elastomers; neutral curing, non - corrosive to most metals; extrusion is excellent, especially suitable for machine glue, glue line smooth and delicate;
Ø Could be matched with RTV-2 automatic glue machine glue, the glue line smooth and delicate;
Ø Excellent resistance to hot and cold alternating performance, aging resistance and electrical insulation properties; adhesive has excellent moisture, quake resistance, corona resistance, anti leakage performance; completely in line with the EU ROHS
● Main Applications:
Ø The sealing adhesive household panel, such as adhesive, microwave oven door glass and metal frame in microwave furnace and the microcrystalline panel bonding.
● Specifications & Packages
Ø 310ml/cartridge, 25cartridges/carton.
Ø 18Kg/bucket, 1bucket/carton
● How to Use
Ø Keep the object surfaces clean without rusts, dusts and oil.
Ø Dispense the sealants to object surfaces.
Ø Put the objects in the air for 24 hours in the condition of room temperature & 55%RH to reach a cure depth of 2~4mm the longer, the deeper.
Ø The outlet of unspent adhesive should be sealed in time, clean the crusts on the outlet for another use within a short time, the performance of adhesive won’t be affected.
● Storage:
Ø Keep the sealant away from children.
Ø Use it in ventilated places
Ø In case of contact with skins, wipe and then flush with clear water.
Ø In case of contact with eyes, flush with clear water immediately and go to hospital for checking.
Ø Store it in dry and shady places at the temperature of 8~28℃
Ø Storage life: A component 12 months and B component 6 months from the date of manufacture.
● Technical Data
Item | Unit | Typical Value | Range |
Item No. | 4010 | ||
Color | Black | ||
Component of Basic Materials | Polysiloxane | ||
Density | g/cm3 | 1.12 | 1.10 ~1.15 |
Tack Free Time (25℃,50%RH) | min | 20 | 20 |
Hardness | Shore A | 40 | 40±5 |
Tensile Strength | Mpa | 1.0 | ≥1.0 |
Elongation at break | % | 150 | ≥150 |
Dielectric Strength | KV/mm | 20 | ≥20 |
Work Temperature | ℃ | -60~200 |