Outdoor LED Screen Thermal Conductive Grease 4120Q RTV Silicone Sealant
|Place of Origin:||CHINA|
Payment & Shipping Terms:
|Minimum Order Quantity:||500KG|
|Packaging Details:||22kg/set: A: 20kg /bucket, B: 2kg/bucket.|
|Payment Terms:||L/C, T/T|
|Supply Ability:||10000KG MONTH|
|Color COMPONENT A:||BLACK||Color Component B:||Translucent|
|Component Of Basic Materials:||Polysiloxane||Density Of A Component:||1.16|
|Density Of B Component:||0.98||Viscosity:||2200|
|Mix Ratio By Weight (A:B):||10:1||Handing Curing Time:||55 Mins|
|Initial Curing Time:||3 Hours||Tensile Strength:||0.6 Mpa|
|Elongation At Break:||160%||Hardness:||Shore A 20|
thermal paste compound,
silicone thermal grease
·4120Q, which is a condensed 2-part silicone sealant and can cure at room temperature, is suitable for molding intricate electronic parts as its low viscosity.
·Otherwise ,it is non-corrosive and suitable for adhering many substrates.
·Suitable for molding intricate electronic parts because of its low viscosity.
·Excellent impact resistance because it forms an elastic silicone rubber after curing.
·Excellent heat resistance, damp resistance and freezing resistance.
·Non- corrosion to the substrate as it is dialcohol curing type.
·Excellent adhesion to many substrates without primer ,especially to PC and Epoxy.
·The fixation and the insulation of the electronic parts.
·Damp-resistance and water resistance for electronic parts and PCB boards.
·Potting of LED displays.
·Other general insulation molding.
● HOW TO USE
·Before mixing, part A should be stirred adequately in container ,and part B should be shaken well in container.
·Before application, you should confirm that its adhesion to
the substrate is well.
·Generally, the mixing ratio of part A and part B is 10 : 1.
If you want to change the curing conditions, a simple test is necessary before used .The curing time and pot life will be decreased while the amount of part B increasing.
·The extra bubble removal is not necessary when molding depth is less than 5 mm. Otherwise , it should be vacuumized at 10mmHg for at least 5 minutes to remove the bubbles. Otherwise, it will influence the surface appearance.
Properties after mixing(25℃,65％RH)
Mixing Ratio(weightratio) A:B = 10:1
Mixture viscosity (cp) 1200
Pot life (min) 30
Curing time (h) 24
Cured 7 d,25℃,65％RH
Durometer Hardness, Shore A 0-5
Tear strength( Kgf/cm2 ) 0.7-0.8
Elongation at break( % ) 160-180
·Packing: A:20kg B:2kg
● USEABLE LIFE AND STORAGE
·When stored at 8-28℃ in the original unopened containers, this product has a usable life of 12 months from the date of production.
·Special precautions must be taken to prevent moisture from contacting Part B. Containers should be kept tighly close.