Product Description
1421 High performance structural bonding acrylic adhesive,two component, blue, rigid, super fast curing
1421 High performance structural bonding acrylic adhesive
Two component, blue, rigid, super fast curing methyl acrylic acid adhesive.Suitable for plastic, metal and composite adhesive, high viscosity, high thixotropic, not vertical flow, Mixing ratio 10:1, Operation time 3-4 minutes, time to 75% strength: 5-7 minutes. Especially suitable for bonding of composite materials, without surface treatment can reach the highest strength, good toughness, good shock resistance, fatigue resistance. Meet the demand of mass production line.
Typical Applications
Transport vehicles, notebook computer, mobile phone and other products such as structural adhesive bonding electrons.
Bonding material: ABS, glass steel, polyester (DCPD modified) polystyrene, polyethylene ester, PVC, polyurethane, coating
Carbon steel, aluminum and stainless steel recommended HuiTian primer 1020.
Cure Exothermic Curve
super fast curing 1421 industrial acrylic Adhesive two component blue ,rigid 23℃,The mixed adhesive 10g
Medium Resistance
Resistance PH 3-10 acid, hydrocarbons, salt solution. Not resistant to polar solvent, acid and alkali.
| Item |
Unit |
Typical Value |
| Color |
Component A |
|
White |
| Component B |
|
Blue |
| Component of Basic Materials |
|
acrylic acid |
| Density |
Component A |
g/cm3 |
0.97 |
| Component B |
1.13 |
| Viscosity |
Component A |
mPa*s |
250000 |
| Component B |
200000 |
| After Mixed |
|
| Mix Ratio by weight (A:B) |
|
10:1 |
| Handing Curing Time |
Min |
55 |
| Initial Curing Time |
Hour |
0.5 |
| Full Curing Time |
Hour |
24 |
| Tensile Strength |
After Curing |
Mpa |
18 |
| Elongation at break |
% |
|
| Hardness |
Shore A |
|
| Volume Resistivity |
Ω*cm |
|
| Dielectric Strength |
KV/mm |
|
| Flame Retardant Rating |
|
UL94 V-1 |
| Work Temperature |
℃ |
-55~82 |
| |
|
|
|
|